Glass kinds might be perplexing to comprehend; yet, the chemical makeup of the glass determines the glass’s qualities. Soda-Lime and Borosilicate glass are two forms of glass that are often used in scientific glassware.

Chemical Composition of Glass

Each glass variety has a distinct chemical makeup, which results in unique properties:

Expansion borosilicate glass — This kind of glass has exceptional resistance to assault by water, acids, salt solutions, halogens, and organic solvents. Hydrofluoric acid, concentrated phosphoric acid, and strong alkaline solutions are the only acids that cause considerable corrosion.

Neutral borosilicate glass — Exhibits superior chemical resistance, making it perfect for storing or packing acidic, neutral, and alkaline items, as well as injectable solutions.

Soda-lime glass – This kind of glass is less resistant to chemical attack than borosilicate glass and is generally used to store dry powders and containers for general sample storage. This glass type has a low resistance to hydrolysis.

Characteristics of Matter

3.3 expansion borosilicate glass is the perfect material for use in labs because of its great chemical toughness, low thermal expansion, and high resilience to thermal shock.

Resistance to Hydrolytic Decomposition

In steam sterilization, for example, frequent exposure to water vapor at high temperatures may cause alkali (Na+) ions to be leached away. Due to the lack of alkali metal oxides in the material, borosilicate glass exhibits a great resistance to water damage.

Resistant to Acid

Acids are less prone to damage glass with high silica content. Expansion in this section It is borosilicate glass that is resistant to acids, with the exception of hydrofluoric acid and phosphoric acid at high temperatures. Class S1 borosilicate glass is one of four acid-resistant glass types.

Water and acids have little effect on the surface of glass. A thin layer of silica gel formed on top of the glass as a result of the little quantity of glass being dissolved.

This layer is prevented from developing, however, by hydrofluoric acid and heated phosphoric acid. Because of the high concentrations and temperatures at which alkalis attack glass, it is possible that volumetric instruments may lose their graduations or have their volumes altered.

The Resistance to Alkali

All forms of glass, including borosilicate, are attacked by alkaline solutions, however borosilicate is rather resistant. Class A2 standards are met by borosilicate glass’s alkali resistance.

Expansion borosilicate glass, such as Pyrex, has good thermal capabilities at both high and low temperatures.

Temperature Resistance

3.3. Laboratory glassware made of borosilicate glass with a 3.3 expansion coefficient should not be used over 500°C (for short periods of time only). Glassware may be damaged by abrupt temperature fluctuations, thus care must be used while heating or cooling.

Glass should be heated to a temperature between the lower and higher annealing points if thermal resistance is a concern. For around 30 minutes, it should be held at that temperature. Afterwards, it has to be cooled down in accordance with the recommended cooling rates.

Although glass has a relatively modest tensile strength, the inclusion of fractures or scratches may significantly increase that strength. The glass should be appropriately heated and cooled in order to maintain its resilience to temperature fluctuations and prevent breaking due to mechanical stresses that are not permitted to be exceeded. Temperature change resistance varies across various kinds of glass.

Maintaining the cleanliness of your laboratory glassware

In order to eliminate any protein residues from the device, begin by rinsing it in cold water. Soak the glassware in the recommended dilution of a disinfectant solution.

Remove any residue on the glass’ surface using a bristle brush. Then take a second soak, or use an ultrasonic bath. Rinse the item three times with deionized water to get rid of any detergent residue. Rack-drain and then bake in a hot air oven in an odorless, sanitary area.